3D kwaze achitekti pore Ti3C2 MXene makonnen ak nanopartikul NiCoP bimetal phosphide

Dènyèman, ekip rechèch Longwei Yin nan Inivèsite Shandong pibliye yon atik sou  Energy & Environmental Science,the title is Alkali-induced 3D crinkled porous Ti3C2 MXene architectures coupled with NiCoP bimetallic phosphide nanoparticles as anodes for high-performance sodium-ion batteries.

Pou amelyore estabilite estriktirèl la ak amelyore sinetik reyaksyon elektwochimik anodik pou sodyòm ion pil (SIBs), yo devlope yon nouvo estrateji pou koup NiCoP bimetalik fosfid nanopartikul ak alkali-pwovoke 3D interkonekte kwochi pore Ti3C2 MXen kòm anod pou pèfòmans SIBs . 

Konekte 3D Ti3C2 achitekti yo pli ka etabli yon rezo konduktif 3D, abondan porositë ouvè ak gwo zòn sifas, ki bay yon gran wout kondiktif 3D ak chanèl debloke pou yon pwosesis transfè rapid chaj ak pou depo elektwolit, epi fè kontak konplètman fèmen ant elektwòd la elektwolit. Estrikti MXene inik la ka efektivman tolere ekspansyon volim ak anpeche agrégation ak pulverizasyon nan nanopartikul NiCoP pandan pwosesis Na + ensèsyon / ekstraksyon. NiCoP fosfid bimetalik la posede pi rich sit reyaksyon redoks, pi wo konduktivite elektrik ak enpedans transfè ki ba. Efè sinèrjetik ant konpozan NiCoP ak MXene Ti3C2 ak estabilite estriktirèl segondè ak aktivite electrochemical mennen nan ekselan pèfòmans electrochemical, kenbe yon kapasite espesifik nan 261.7 mA hg -1  nan yon dansite aktyèl la nan 1 A g -1  pou 2000 sik. Estrateji a prezan nan yon  situ ak kouple fosfid ak 3D 3D Ti3C2 ka pwolonje nan lòt elektwòd roman pou pèfòmans-wo aparèy depo enèji.


Post tan: Nov-18-2020